Normes de mise en œuvre : tuyaux en acier sans soudure GB/T8162 pour la structure, tuyaux en acier sans soudure GB/T8163 pour le transport des fluides. Propriétés mécaniques 0420D et 0420E : résistance à la traction 520~680MPa,<16 service strength 2420MPa, 16mm~30mm service strength 2400, 230mm Yield strength 2380MPa Impact test Q420D minus 20C Impact energy 234, impact test Q420E minus 40C Impact energy 227 :0.20, chromium: <0.30, nickel: <0.50, copper: 0.20, nitrogen: 0.015, :0.20, aluminum, 20.015.Q420E seamless steel pipe chemical composition: carbon: 0.20, silicon: 0.50, :1.70, phosphorus: 0.025, Sulfur: 0.020, : 0.07, : 0.20, : 0.20 Chromium: <0.30, Nickel: <0.50, Copper: <0.20, Nitrogen: 0.015, : 0.20, Aluminum, 20.015. Steel refining method: Steel should be processed by electric arc furnace Refining outside the furnace or gas converter plus outside refining method. After negotiation between the supply and demand parties, other methods with higher requirements can also be used to treat refining. When the demander requires a certain refining method, it should be stated in the contract.
Méthode de fabrication des tuyaux : Les tuyaux peuvent également être fabriqués par coulée continue, moulage en moule ou laminage à chaud.
Les tuyaux en fonte continue doivent également être conformes aux réglementations YB/T 4149 ; les tuyaux chauds doivent également être conformes aux réglementations YB/T 5221 ou YB/T 5222 ; les tuyaux moulés peuvent également faire référence aux réglementations relatives aux tuyaux chauds (forgés).